Description
Carbon Nanotube Masterbatches CNT-PA6-15
Our carbon nanotube masterbatches CNT-PA6-15 use our industrial grade multi walled carbon nanotubes. This product has a 15% CNTs loading ratio.
The CNT-PA6-15 material can be used with 3D printers, injection molders, & extruders. Once received, you simply let it down and run it in your equipment. Sold by the kilogram
|
Product Code
|
Matrix Resin |
Matrix Resin Loading |
CNTs Code |
CNTs Loading |
|
CNT-PA6-15 |
PA6 |
85wt% |
IGMWNTs 20-40nm |
15wt% |
CNT-PA6- 15 was dispersed in PA6 using twin-screw extruder, the pellets are made by injection molding. Volume and surface resistivity were measured by high insulation resistance instrument ZC-90D（IEC 60093-1980, the test voltage is 100V）.
|
CNTs Loading（wt%）
|
2 |
3 |
|
Volume Resistivity (ohm.cm) |
2.2×1012 |
6.3×107 |
|
Surface Resistivity (ohm) |
1.6×1013 |
2.7×107 |
CNT-PA6-15 was diluted by PA6 using twin-screw extruder, then the specimens were made by injection molding. The standard of mechanical property of specimens was ISO 527, ISO 180 and ISO 178.
|
CNTs Loading（wt%）
|
0（Pure PA6） |
3 |
|
Tensile Strength（MPa） |
62.6 |
71.4 |
|
Stain at break（%） |
52.9 |
17.8 |
|
Izod Notched Impact Strength（KJ/m2） |
7.9 |
4.1 |
|
Flexural Strength（MPa） |
77.5 |
82.6 |
|
Flexural Modulus（MPa） |
1696 |
1940 |